Jaan Laid

Vassil, Jaan, Paul, poeg, 1936, mitte küüditatud. http://www.okupatsioon.ee/et/memento-2001/239-v-2001

Elulugu: http://deepzone2.ttu.ee/soojus/elulood/elujlaid.pdf

JAAN LAID

27.02.1936 – 22.10.2004

Tehnikakandidaat / Candidate of Technical Sciences

Jaan Laid oli sündinud 27. veebruaril 1936 Pärnus, isa oli jurist, ema lasteaednik. Ta abiel-lus 1964 Mare Saarts’iga. Perre sündis 1970 poeg Mart ja 1972 tütar Riina.

Haridustee ja teenistuskäik. Õpinguid alustas J. Laid 1944 Pärnu I Keskkoolis ja lõpetas sama kooli 1955. Samal aastal asus ta õppima Tallinna Polütehnilise Instituudi laevajõu-seadmete erialal, mille lõpetas 1961 cum laude diplomiinsenerina. Pärast lühiajalist 1961–1963 töötamist insener-konstruktorina Tallinna Meretehases, astus ta 1963 aspirantuuri TPI soojusenergeetika kateedris, mis jäigi edaspidiseks tema teadustöö ja inseneriloomingu ainsaks tööpaigaks, esialgu nooremteaduri ametkohal ja seejärel kuni elu lõpuni vanemtea-durina.

Teaduslik uurimistöö. J. Laidi esimene uurimistöö, mille juhendaja oli tehnikakandidaat dotsent Paul Anson, oli seotud tollel ajal vägagi aktuaalse energotehnoloogilise põlevkivi põletamise probleemiga. Teadlaste tähelepanu köitis seejuures põlevkivituhk, millest võis labori katsete põhjal peale mõnede lisandite manustamist saada kvaliteetset tsemendiklink-rit. Probleemi tööstuslik lahendus võinuks seisneda vedelšlakkrežiimil töötava põlevkivi-katla loomises, mille koldest väljuva vedelšlaki kiirjahutamisel tekiks tsemendiklinker.

Järgnes mahukas töödetsükkel, milles käsitleti katlateraste kõrgtemperatuurset korrosiooni. See temaatika köitis J. Laidi sedavõrd, et sellest sai pikaks ajaks tema uuringute põhiprob-leem.

Kui Kohtla Järve Soojuselektrijaamas valmis katsestend, mis võimaldas saada kõrg-temperatuurset õhku (kuni 800°C) tagamaks põlevkivi põlemist vedelšakkrežiimil, sai sel-lest J. Laidile uurimistöö üks esimestest katseseadmetest. Kõrgtemperatuurse küttepinna korrosiooniuuringud sellel katseseadmel andsid korrosiooniuuringutele uue suuna, mis senini oli jäänud tähelepanuta, nimelt – põlemisgaasi temperatuuri mõju metalli korrosioo-nikiirusele. Jätkamaks neid uuringuid ja saamaks täpsemaid katseandmeid projekteeris ja ehitas ta katsestendi, millel hakkas uurima teraste korrosiooniintensiivsuse sõltuvust metal-lipinna ja seda uhtuva põlemisgaasi temperatuurist vedelkütuste põletamisel, kasutades seejuures nii vanaadiumivaba põlevkiviõli kui ka erineva vanaadiumisisaldusega rasket kütteõli. Sellest tööst huvitus väga Taganrogi Katlatehas. Koostöös J. Laidiga valmis Ta-ganrogi Katlatehase peakonstruktoril L. M. Hristitšil tehnikakandidaadiväitekiri „Masuudi põlemisgaasi temperatuuri mõju küttepinna metalli gaasipoolsele korrosioonile”, mille kaitses TPI soojusenergeetika kateedri erialanõukogus 1971.

J. Laidi kandidaadiväitekiri valmis mitme terasemargi korrosiooniuuringute tulemusena, mis viidi läbi nii Kohtla-Järve kõrgtemperatuurses õhueelsoojendis kui katsestendil. Väite-

kirja kaitses ta TPI soojusenergeetika kateedri erialanõukogu ees 1975. Väitekirjas esiletõs-tetud üks järeldustest – „isegi vanaadiumi tühine sisaldus vedelkütuses põhjustab energee-tikaseadme metallile ülitõsiseid korrosioonikahjustusi juhul kui metalli temperatuur on kõrgem kui 600°C” – on pälvinud laialdast tunnustust.

J. Laidi projekteeritud ja valmistatud seadeldis mõõtmaks küttepinna torust väljalõigatud rõngakujulise katsekeha põlemisgaasipoolse korrosioonikahjustuse sügavust on tähelepa-nuväärne leiutis ning võetud kasutusse korrosiooniuuringutega tegelevates asutustes.

Koostöös tehnikakandidaat Heinrich Suigiga uuris J. Laid elektrijaama suure võimsusega õliküttekatlasse paigutatud pooltööstusliku katseküttepinna korrosiooni olenevust põlemis-gaasi ja metallipinna temperatuurist ja ajast. Pikka aega väldanud katsete andmetöötlus võimaldas luua terase korrosiooniprotsessi mitmeparameetrilise matemaatilise mudeli ja selle toel tuletada valemid arvutamaks metalli korrosioonikiirust vedelkütuse põlemisgaasi keskkonnas.

J. Laidil on ka tähelepanuväärseid teeneid kroomkattega katlatorude kõrgtemperatuurse korrosiooni uuringute valdkonnas. Ta tuletas matemaatilise avaldise määramaks analüütili-selt difusioonkroomkattega katlatorude korrosioonikiirust. Ta tõestas, et kroomkate on eriti tõhus, kui küttepind paikneb intensiivse kiirguse piirkonnas.

Leiundustegevus. Läinud sajandi lõpupoolel elavnes TTÜ STIs uurimistegevus biokütuste põletamise valdkonnas. Selle töö käigus konstrueeriti mitu uuetüübilist keskküttekatelt, põletit ja kütuse laondusseadet, mille väljatöötamisel ja katsetamisel oli Jaan Laid põhitegi-ja. Nendesse aastatesse kuulub väikekatla uue seeria väljatöötamine. Kumerate torulauda-dega leek-suitsutorukatel on J. Laidi kui andeka leiutaja ja võimeka konstruktori loomingu ilmekas näide. Selle katla projekteerimisel kasutatud uudsed konstruktsioonilahendused on esitatud teadusartiklites ja on toonud autorile mitu Eesti kasuliku mudeli tunnistust. Seda tüüpi väikekateldel „Malle” ja „Pelle” on hea maine ja nad on omandanud kindla koha AS Viljandi Metallitööstuse toodangus.

Aastate jooksul on Jaan Laid olnud autoriteetne ekspert katla tugevus- ja kontrollarvutuse alal, tema allkiri on paljude katla ümberseadistusprojektide ja eksperdihinnangute all. Tema arvamused katla käitusküsimustes olid läbimõeldud ja alati arvestatavad. Samuti jätkus tal huvi ka hoonete soojusvarustuse ja keskkütte vastu.

Lisaks põhitööle õpetas Jaan Laid soojuserialade üliõpilastele katlatehnika kursuses katla-metalli omadusi ja kasutusvaldkondi.

Koos kaasautoritega on Jaan Laid avaldanud 51 publikatsiooni, sh viis autoritunnistust.

Jaan Laid suri 23. oktoobril 2004 ja on maetud Tallinna Metsakalmistule.https://www.kalmistud.ee/haudi?action=hauaplats&filter_hauaplats_ha...

Kandidaadiväitekiri – „Kõrgtemperatuurse küttepinna korrosioon energeetilise vedelkütuse põletamisel” (Corrosion of high temperature heating surfaces in burning liquid fuels), TPI, 1975.

• * *

Jaan Laid was born on the 27th of February, 1936, in the city of Pärnu. His father was a lawyer and his mother was a kindergarten teacher. On July 10th, 1964, he married Mare Saarts. In 1970 son Mart was born and in 1972 – daughter Riina.

Education and career. Jaan Laid started his education in 1944 at the Secondary School No 1 of Pärnu and graduated from this school in 1955. In the same year he became a student of Tallinn Polytechnic Institute, specialising in ship energy installations. He graduated cum

laude with an engineering degree in 1961. After a brief period 1961-1963 of work as engi-neer-designer at Tallinn Marine Factory and having acquired experience in designing that proved very useful for his subsequent career, he became a post-graduate student at the Chair of Thermal Engineering of TPI (later the Department of Thermal Engineering of TUT) in 1963. There he conducted scientific research and engineering design work for the rest of his life, first as junior and then as senior research scientist.

Jaan Laid’s first research work, supervised by Associate Professor Paul Anson, technical science candidate (Ph.D), was connected with a vital energy engineering issue of that time – oil shale combustion. The scientists’ attention was focused on oil shale ash because, based on laboratory trials, this ash could be made into a quality cement clinker with the introduction of some additives and fusion. The industrial solution for the issue could be the development of an oil shale boiler operating in the liquid slag regime – as the liquid slag leaving the furnace is rapidly cooled, it turns into a cement clinker.

This premise was followed by an extensive research cycle examining boiler steel high-temperature corrosion. This topic attracted J. Laid even so that it remained the main theme of his research for a long time.

With the completion of a test board at the Kohtla Järve Thermal Power Plant, enabling the supply of high-temperature air (up to 800°C) to ensure that oil shale is combusted in the liquid slag regime, it became one of the first trial devices in J. Laid’s research. The high-temperature heating surface corrosion tests conducted on this device gave a new direction to the boiler metal corrosion studies. This aspect – how the flue gas temperature influences the metal corrosion speed – had previously been overlooked. To continue this research and obtain more precise test data, he designed and built a special test board for boiler steel corrosion studies, on which he began examining how the steel corrosion intensity depends on the temperature of the metal surface and the flue gas that flushes it during liquid fuel combustion. For that purpose he used both vanadium-free oil shale oil and heavy fuel oil with different vanadium content levels. The Taganrog Boiler Factory became very inter-ested in this work. Cooperating with J. Laid, L. Khristich, Chief Designer of the Taganrog Boiler Factory, completed the technical science candidate degree thesis “Influence of the heavy fuel oil flue gas temperature on the heating surface’s gas-side metal corrosion”, successfully defending it in 1971 at the specialty council of the Chair of Thermal Engineer-ing of TPI.

Jaan Laid’s candidate degree thesis was completed as a result of corrosion trials of several steel brands, carried out both at the Kohtla Järve high-temperature air preheater and at the test board. He successfully defended the thesis in 1975 at the specialty council of the Chair of Thermal Engineering of TPI. One of the conclusions reached in the thesis – “even an inconsiderable vanadium content in liquid fuel causes extremely serious corrosion dam-age in power engineering devices’ metal when its temperature exceeds 600°C” – earned wide acknowledgement.

The apparatus designed and built by J. Laid to measure the corrosion damage depth on the flue gas side of a ring-shaped test sample cut out from a heating surface pipe is a remark-able invention and has been adopted by institutions conducting corrosion studies.

Cooperating with Heinrich Suik, technical science candidate, J. Laid examined how corro-sion of steel on semi-industrial test heating surfaces installed in a large-capacity oil fuel power plant boiler depends on the temperature/time of the flue gas and the metal surface. When the data from these long-term trials had been processed, it enabled the researchers to

create a multi-parameter mathematical model of the steel corrosion process and on the basis of this model to derive formulas for calculating the metal corrosion steel in the liquid fuel flue gas environment.

J. Laid also made notable contributions in the sphere of research into high-temperature corrosion of chrome-coated boiler pipes. He derived a mathematical expression to analyti-cally determine the corrosion speed of boiler pipes with diffusion chrome coating. He proved that the chrome coating was especially efficient when the heating surface was lo-cated in an area of intense emission.

Towards the end of the 20th century the Department of Thermal Engineering became in-creasingly actively involved in the biofuel combustion research sphere. Several new-type heating boilers, burners and fuel storage devices were constructed, Jaan Laid being the central figure in their development and testing. During that time a new small boiler series was also developed. The flame-flue boiler with convex pipe planks is a perfect example of his work as a talented inventor and a capable designer. The innovative design solutions used in the development of this boiler were described in scientific articles and resulted in several Estonian utility certificates for the author. The small boilers of this type, called “Malle” and “Pelle”, have a good reputation and have become a constant part of the product range offered by Viljandi Metallitööstuse AS.

Through the years, Jaan Laid was always a competent expert in the field of boiler strength and reference calculations, his signature can be found on many boiler readjustment pro-jects and expert evaluations. His opinions on boiler functioning issues were well-considered and always reckoned with. He also expressed interest in heat supply for build-ings and central heating.

In addition to his main job, Jaan Laid taught boiler metal properties and application spheres as part of the boiler technical course to students specialising in thermal engineer-ing.

Jaan Laid was author and co-author of 51 printed publications, including five patents.

Jaan Laid died on the 23rd of October, 2004, and was buried at the Metsakalmistu Ceme-tery in Tallinn.

Candidate’s degree dissertation: Corrosion of high temperature heating surfaces in burn-ing liquid fuels, TPI, 1975.